Electronic structure modulation of iron sites with fluorine coordination enables ultra-effective h2o2 activation

ABSTRACT Electronic structure modulation of active sites is critical important in Fenton catalysis as it offers a promising strategy for boosting H2O2 activation. However, efficient

generation of hydroxyl radicals (•OH) is often limited to the unoptimized coordination environment of active sites. Herein, we report the rational design and synthesis of iron oxyfluoride

(FeOF), whose iron sites strongly coordinate with the most electronegative fluorine atoms in a characteristic moiety of F-(Fe(III)O3)-F, for effective H2O2 activation with potent •OH

generation. Results demonstrate that the fluorine coordination plays a pivotal role in lowering the local electron density and optimizing the electronic structures of iron sites, thus

facilitating the rate-limiting H2O2 adsorption and subsequent peroxyl bond cleavage reactions. Consequently, FeOF exhibits a significant and pH-adaptive •OH yield (~450 µM) with high

selectivity, which is 1 ~ 3 orders of magnitude higher than the state-of-the-art iron-based catalysts, leading to excellent degradation activities against various organic pollutants at

neutral condition. This work provides fundamental insights into the function of fluorine coordination in boosting Fenton catalysis at atomic level, which may inspire the design of efficient

active sites for sustainable environmental remediation. SIMILAR CONTENT BEING VIEWED BY OTHERS ROBUST FE-N4-C6O2 SINGLE ATOM SITES FOR EFFICIENT PMS ACTIVATION AND ENHANCED FEIV = O

REACTIVITY Article Open access 10 March 2025 COORDINATION ENGINEERING OF HETEROGENEOUS HIGH-VALENT FE(IV)-OXO FOR SAFE REMOVAL OF POLLUTANTS VIA POWERFUL FENTON-LIKE REACTIONS Article Open

access 19 November 2024 IRON PHTHALOCYANINE WITH COORDINATION INDUCED ELECTRONIC LOCALIZATION TO BOOST OXYGEN REDUCTION REACTION Article Open access 20 August 2020 INTRODUCTION Clean water

scarcity originating from rapid urbanization and heavy industrialization becomes one of the most severe challenges to sustainable society at a global scale1,2,3,4,5,6. It is imperative to

explore highly efficient and economically affordable water purification technologies, especially relying on reactive oxygen species generation for pollutant degradation7,8. The

metal-mediated Fenton catalysis based on H2O2 activation have been deemed a promising strategy for water decontamination due to its high efficiency and easy operation9,10,11. However, it has

several drawbacks that limit further applications, such as harsh operation pH, low H2O2 utilization, metal-rich sludge, and unsatisfactory stability12,13,14. In addition, the insufficient

•OH production and marginal H2O2-to-•OH selectivity during Fenton catalysis processes leads to substantial chemical inputs and undesirable by-products formation9,11,15,16. To tackle these

shortcomings, heterogeneous Fenton catalysts focusing on the microenvironment modulation of active sites via facet, heteroatom, defect, and single-atom engineering have been well-designed

and developed to promote H2O2 activation13,17,18,19. Unfortunately, decomposing H2O2 molecules into •OH radicals with high yields and selectivity during Fenton catalysis remains great

challenging, especially under a neutral condition. Recently, 2D van der Waals transition-metal oxyhalides, an emerging layered nanomaterials with charming physicochemical properties, have

attracted widespread interest in catalysis, energy, and environmental remediation fields20,21,22,23,24. Among various metal oxyhalides, iron oxychloride (FeOCl) having octahedral FeO4Cl2

layers held by Cl−Cl van der Waals interaction is recognized as a landmark candidate for H2O2 activation at pH 7.0 because it exhibits high efficiency in the homolytic cleavage of H2O2

molecules with the highest •OH generation capacity so far9,25. From a mechanical perspective, the electro-withdrawn effect of Cl and O atoms coordination to active iron sites enables the

reduction of local electron density via polarization effect9,26. This specific coordination regime contributes most in promoting Fe(III) species reduction as well as H2O2 decomposition

toward •OH radicals. Afterward, significant endeavors have been made to further improve the activation performance of FeOCl by doping, intercalation, and nanoconfinement engineering while

most fails to optimize •OH radical yields with satisfactory selectivity27,28,29. Interestingly, the K+ intercalation into FeOCl alters the H2O2 activation pathway from •OH radicals to Fe(IV)

 = O species with improved tolerance to water matrix while the oxidation efficiency may be partially compromised30. In principle, H2O2 activation mainly relies on the peroxyl bond cleavage

induced by electron transfer between active sites (e.g., iron sites) in catalysts. The electron transfer efficiency could be regulated by tuning the coordination environment of active sites,

which allows for the optimization of electron states (e.g., charge density) that govern Fenton catalysis performance8,14,31,32. Recently, substantial efforts have been made to optimize the

microenvironmental of metal active sites with rapid electron transfer and decode the mechanisms of free radical conversion by doping heteroatoms with strong electron-withdrawing functions.

For instance, boron, phosphorus, oxygen, and sulfur-doped single-metal atoms with lowered local electron density demonstrate a dramatically enhancement of typical oxidants (e.g., H2O2,

peroxymonosulfate, peracetic acid, etc.) activation over analogy counterparts for boosting organic pollutant degradation13,18,33,34,35. Surprisingly, the manipulation of active iron sites in

the FeOCl matrix is often overlooked. Scarce efforts have devoted to introducing such electronegative moieties while great attempts have made to delivery FeOCl composites for application

development despite of its relatively low •OH yields (e.g., 11 μM) and H2O2 utilization (e.g., ~0.73‰ of •OH selectivity)9. Inspired by above trails, we speculate that it is feasible to

regulate the local electron density of iron sites by coordinating highly electronegative atoms to large improve the Fenton catalysis performance. F (3.98) is the most electronegative element

in earth, and it shows the highest electron-withdrawing activity than B (2.04), P (2.19), S (2.58), N (3.04), and Cl (3.16)35. To this end, switching Cl atoms of O-Fe-Cl bonds with F atoms

to form a O-Fe-F unique coordination would be expected to efficiently optimize the electron density of iron sites and thus enhance the H2O2 activation performance. Herein, we rationally

designed and synthesized FeOF as a powerful catalyst, in which fluorine atom strongly coordinates to iron sites in a characteristic moiety of F-(Fe(III)O3)-F, for enabling effective Fenton

catalysis with potent •OH generation. By systematically comparing the local electronic structure and Fenton catalysis behaviors of FeOF and FeOCl via both theoretical calculation and

experimental analysis, we observed that the strong electron-withdrawing ability of coordinated fluoride atom could largely reduce the local electron density of iron sites and thus the energy

barrier of rate-limiting step in H2O2 activation was greatly lowered. Intriguingly, the FeOF featuring such specified unique coordination environment allows for efficient •OH generation (up

to ~450 μM yield and 33.2% selectivity), significantly outperforming FeOCl analogy and the state-of-the-art Fenton catalysts ever recorded. Moreover, the excellent practicality regarding

degradation capability, cyclic stability, and wastewater treatment potential of the FeOF/H2O2 Fenton process was also systematically demonstrated. This work not only affords the rational

design principle for Fenton catalysts at the atomic scale but also provides fundamental insights into the enhancement mechanism of H2O2 activation. RESULTS SYNTHESIS AND CHARACTERIZATIONS OF

FEOF CATALYST The FeOF catalyst was prepared by obtaining FeSiF6 · 6H2O from dissolving iron powders in fluorosilicic acid (H2SiF6) aqueous solution, followed by a simple solvothermal

reaction (Fig. 1A). Representative X-ray diffraction (XPD) patterns that clearly well matched the standard cards (PDF #26-0799 and #70–1522) without additional peaks in Supplementary Fig. 1

and Fig. 1B confirmed the successful fabrication of FeSiF6 · 6H2O and FeOF catalyst with moderate crystallinity36,37. The downshift of (111) and (211) facets in the recorded pattern might be

assigned to the presence of oxygen vacancy that expands the crystal lattice38,39,40. As illustrated by high-resolution transmission electron microscope (HRTEM) image in Fig. 1C, a lattice

finger distance of 2.24 Å and 1.71 Å (Supplementary Fig. 2B and Fig. 1C) representing the (111) and (211) facets of FeOF can be observed37, further supporting the XRD result. The FeOF

catalyst displayed a collective sphere-like framework with a diameter size of ca. 300 nm, constructed from smaller nanoparticles (ca. 20~50 nm), as demonstrated by the field-emission

scanning electron microscopy (FE-SEM) images (Supplementary Fig. 3) and TEM images (Supplementary Fig. 4). To our delight, the element mapping in the high angle annular dark-field scanning

TEM (HAADF-STEM) image and energy dispersive X-ray spectroscopy (EDS) analysis of the prepared FeOF (Fig. 1D) verify the uniform distribution of Fe, O, and F elements. Moreover, the

distinctive chemical bonding signals in the spectra (Supplementary Fig. 5) was recorded and clarified using Fourier Transform Infrared Spectroscopy (FT-IR) and X-ray photoelectron

spectroscopy (XPS). Specifically, the high-resolution XPS spectrum of Fe 2_p_ (Fig. 1E) exhibited two deconvoluted peaks at 728.9 and 715.7 eV, attributing to the Fe 2_p_1/2 and Fe 2_p_3/2

in Fe(III). The distance of 13.2 eV over these two peaks and the observed shakeup satellite at 722.2 eV indicated the main existence of Fe(III) in FeOF catalyst11,41. The peaks referring to

iron species in FeOF suffered an obvious shift to a higher binding energy against those in FeOCl, suggesting the electron density around iron sites was largely reduced by fluorine

coordination42,43,44, which would improve the interaction between H2O2 molecules and iron sites. A distinguishing type-IV hysteresis loop can be found in the obtained N2

adsorption-desorption isotherms (Supplementary Fig. 6) of FeOF catalyst, indicative of inherent mesoporous structure (Supplementary Table 1) that can facilitate mass transfer and catalytic

efficiency45. By comparison to FeOCl (Supplementary Fig. 7), the smaller particle size and higher surface area of FeOF are conducive to Fenton reaction by increasing the density and

accessibility of active iron sites. As previous reports demonstrated, the Fenton catalysis activity depends highly on the surface Lewis acid site originating from the inherent coordination

environment of iron centers46. Therefore, we first performed pyridine-chemisorbed in-situ FT-IR (Py-IR) under three typical degassing temperatures (i.e., 50, 100, and 200 °C) to unravel the

Lewis acidity of FeOF catalyst and systematically compare with its analogy FeOCl. The characteristic diffraction signals in XRD pattern (Supplementary Fig. 7A), nanosheet morphology in

FE-SEM images (Supplementary Fig. 7B–D), and porous structures of FeOCl (Supplementary Fig. 6) suggested its well synthesis for comparison according to the landmark study9. These findings

confirmed the structural congruence between FeOF and FeOCl for both molecular and crystal aspects. It can be found that Py-IR spectra for FeOF (Supplementary Fig. 8A) and FeOCl

(Supplementary Fig. 8B) exhibit two typical IR bands at 1445 and 1480 cm−1, which were all attributed to a pyridine-Lewis acid adduct46,47,48. Whereas, no distinct band detected at ~1540 

cm−1 excludes the appearance of Brønsted acid sites46. In addition, as degassing temperature increased, the band intensity in the Py-IR spectra of FeOF suffered a moderate decrease while a

dramatic decline occurred for FeOCl. These results demonstrated that the surface of FeOF was covered by a large amount of stronger Lewis acid sites than that of FeOCl, which primarily

identified the effect of higher electronegativity of fluoride on significantly reducing the local density electron of iron sites. For a more direct comparison, the Lewis acidity of different

acid types including weak, medium, and strong, revealed by the Py-IR spectra recorded at different degassing temperatures, was quantified according to previous reports46,49,50, and

summarized in Fig. 1F. The total Lewis acidity for FeOF was calculated to be 3.037 mmol g−1, in which the weak (0.004 mmol g−1), medium (1.702 mmol g−1), and strong (1.332 mmol g−1) site

make up 0.1%, 56.0%, and 43.9%, respectively. In contrast, the FeOCl showed a one in three Lewis acidity (1.068 mmol g−1) toward FeOF, consisting of 41.2% weak and 56.9% medium sites.

Therefore, it is supposed that FeOF is more favorable for Fenton catalysis as it contains high proportion of medium and strong Lewis acid sites that can facilitate the interaction with H2O2

for sustainable activation through the enhanced the Fe(III)/Fe(II) redox cycle12,32,51,52. COORDINATION ENVIRONMENT AND ELECTRONIC STRUCTURE To gain a molecular structure insight into the

Lewis acid site, the 57Fe Mössbauer spectroscopy was employed to discriminate different iron species in FeOF. As demonstrated in Fig. 1G and Supplementary Table 2, the 57Fe Mössbauer

spectrum of FeOF shows two fitted doublets, i.e., D1 and D2, both of which have an isomer shift (IS) lower than 2.0, suggesting that iron exists in the form of trivalent state as XPS result

revealed53,54. Importantly, D1 with relatively larger values of IS and quadrupole splitting (QS) values can be assigned to the F-(Fe(III)O4)-F high-spin structure with saturated

hexa-coordination numbers, in which F atoms were shown in _cis_-conformation54. The structure is so robust that it is hardly employed as active sites for H2O2 activation. Whereas, D2 having

smaller IS and QS values can be attributed to the F-(Fe(III)O4) or F-(Fe(III)O3)-F medium-spin structure53. Such an unsaturated coordination structure of D2 with fluoride as a mediator for

the local electron density of iron sites enables it to be catalytically active for effective Fenton catalysis. The quantitative analysis suggested that the contents of D1 and D2 site were

54.0% and 46.0%, respectively, proving the predominance of unsaturated iron coordination structure (i.e., F-(Fe(III)O4) or F-(Fe(III)O3)-F moiety) in FeOF catalyst. To further elucidate the

local structure information at the atomic level, we examined the electronic structure and coordination environment of iron sites by X-ray absorption spectroscopy (XAS). As shown in Fig. 2A,

Fe K-edge X-ray absorption near-edge structure (XANES) spectra indicate that the absorption energy of FeOF was evidently dissociate to Fe foil but intimate to Fe2O3 and FeF3, implying that

Fe species in FeOF carries positive charge toward +341. Noteworthily, the valence of Fe species was calculated to be +2.95 based on the linear fitting curve (Fig. 2B) of Fe valence versus Fe

K-edge energy that determined from maximum in the first-order derivative. This indicated the popularity of Fe(III) and the presence of limited amount of oxygen vacancies in FeOF. Moreover,

the lower normalized intensity of white peak locating at near-edge (7130.2 eV) in the XANES spectrum of FeOF implied the five-fold coordination by F and O atoms for unsaturated coordination

iron sites53,55. To clarify the atomic configuration of iron species in FeOF, the extended X-ray absorption fine structure (EXAFS) spectrum was further analyzed by the Fourier transformed

(FT) k3-weighted _χ_ (k) function (FT-EXAFS). As depicted in Fig. 2C, the FT-EXAFS curve of FeOF presents two main peaks at 1.5 and 2.5 Å, which were assigned to the Fe-F/Fe-O and Fe-Fe

shells, respectively53. Wavelet transform (WT) was also applied to evaluate the Fe K-edge EXAFS oscillations of FeOF and the references (i.e., Fe foil, FeO, Fe2O3, Fe3O4, and FeF3). As

displayed in Fig. 2E, we can clearly observe a WT maximum at ּ~8.1 Å−1 that corresponds to the Fe-Fe configuration in Fe foil rather than in FeOF. Comparative intensity maximum at ּ~5.1 Å−1

for FeOF suggested the co-existence of Fe-F and Fe-O coordination bonds as the presence of fluoride atom enables a slight shift toward higher Å−1 than individual Fe-O coordination bond found

in pure Fe2O3 reference (~4.2 Å−1). According to WT-EXAFS features on FeF3, the location of WT maximum for Fe-F bond is similar with that on FeOF, highlighting the presence Fe-F bond in

FeOF. Moreover, a least-square fitting of EXAFS and FT-EXAFS was conducted to obtain quantitative structural parameters of iron site in FeOF and the references. The fitting curves are

illustrated in Fig. 2D, and the obtained structural parameters are summarized in Supplementary Table 3. The double-shell fitting based on the Fe-F and Fe-O coordination models that extract

from FeF3 and Fe2O3 conformed well to the experiment result, manifesting the F, O dual coordination for the iron site in FeOF. The coordination numbers of F and O atoms for the iron site

were determined to be 1.9 and 2.7 at distances of 1.99 and 1.90 Å, respectively, which is similar to the coordination environment of FeOCl (~1.8 Cl atoms and ~3.5 O atoms) demonstrated by a

previous report56. This observation justified the characteristic moiety of F-(Fe(III)O3)-F in the fine local structure elucidation of FeOF, which was consistent with Mössbauer spectroscopy

and XANES analysis. Inspired by above analysis, we compared the electronic structures of FeOF and FeOCl catalysts using density functional theory (DFT) calculations. The applied molecular

structure geometries of FeOF and FeOCl after optimization for electron density calculations are illustrated in Supplementary Fig. 9A. Given its much higher electronegativity than chlorine

atom, the fluoride atom in the as-prepared FeOF enables to alter and optimize the electronic structure of active iron sites. This can be proved by the differences between the two-dimensional

valence-electron density color-filled maps of FeOF and FeOCl. Therefore, we first depict the corresponding two-dimensional valence-electron density color-filled maps in Supplementary Fig. 

9B. Evidently, the largest electronic distribution area emerged around fluoride atom for FeOF and chloride atom for FeOCl. The preferential electron flow from Fe toward themselves due to the

higher electronegativity than another coordination oxygen atom. The chloride and fluoride atom possess relative higher negative-charge while the neighboring coordinated iron center presents

considerably lower electron density. In particular, the maximum valence-electron density of iron center in FeOF was ca. 0.04 _e_ Å−3 (Supplementary Fig. 10), which was 5 times smaller than

that in FeOCl (ca. 0.20 _e_ Å−3), theoretically confirming the extensive modulation effect of the fluoride atom through strong polarization. Moreover, the valence state analysis indicated

that the iron center loses ca. 1.71 _e_ mainly transferring to the neighboring fluoride atom in FeOF while the chloride atom in FeOCl only triggered ca. 0.43 _e_ withdrawn from the

neighboring iron center with a total loss of ca. 1.47 _e_ (Supplementary Fig. 9B). These results strongly supported our speculation that the highest electronegative fluoride atom allows for

the large reduction of local electron density of iron sites, thereby improving the Fenton catalysis activity, which was further discussed in next section. FENTON CATALYSIS PERFORMANCE

EVALUATION The generation of •OH is one of the most significant descriptors to evaluate the performance of H2O2-based Fenton catalysis. We thereby qualitatively and quantitatively

investigated the •OH generation of FeOF and FeOCl catalysts using electron paramagnetic resonance (EPR) technique and fluorescence method, respectively. While using 5,5-dimethyl-1-pyrroline

N-oxide (DMPO) as a trapping agent, we observed four distinctive EPR peaks (Fig. 3A) with an intensity ratio of 1:2:2:1 for the DMPO-•OH adduct, confirming the production of •OH in both FeOF

and FeOCl samples11,57. Notably, the relative intensity of EPR signals in the neutral FeOF/H2O2 system largely outcompeted that of FeOCl/H2O2 counterpart. This result suggested that the

rationally designed FeOF exhibit much better Fenton catalysis performance than FeOCl. Moreover, the intensity of characteristic signals in FeOF (Supplementary Fig. 11) could be largely

declined with the addition of tert-butanol (TBA), a typical •OH scavenger58. This further indicated the ascendency of •OH generation in H2O2 activation using FeOF. However, the addition of

10 mM of TBA fails to completely quench the generated •OH, implying the formation of small amount of surface-bounded •OH (•OHsurf). Impressively, similar EPR signals of DMPO-•OH adduct were

recorded in the Fenton catalysis process under various pH conditions (Supplementary Fig. 12), confirming the production of •OH at a wide pH range. This observation demonstrated that the

as-prepared FeOF catalyst is expected to exhibit a broader application in different water matrixes conditions due to its high pH-adaptability, which is a long-term pursued goal in reforming

Fenton chemistry because the negative effect of harsh operation pH is difficult to overcome. Enlightened by these results, we deduced that the fluoride atom coordinated to active iron sites

enables the as-prepared FeOF to selectively activate H2O2 with a greater ability than that of FeOCl, showing a more promising potential for Fenton catalysis with high pH-adaptability. To

quantify •OH generation, a fluorescence method59 using coumarin as the probe was subsequently conducted to examine the specific activity of FeOF and its analogy FeOCl. As depicted in Fig. 

3B, C, we observed a margin •OH generation with a normalized rate of 0.12 μM min−1 in FeOCl/H2O2 system at the first 15 min while the accumulated concentration reached to 2.1 μM at 120 min,

which is consistent with previous reports9,25. In contrast, FeOF/H2O2 system exhibited a rapid •OH generation with a normalized rate of 2.94 μM min−1 and an accumulated concentration of

353.0 μM, which were 17.5 and 168.0 times higher than that of FeOCl/H2O2 system. We also excluded the homogeneous contribution of leached iron ions because scarce •OH was generated when

using Fe2+, Fe3+, and Fe2+/Fe3+ mixture as the catalyst at equivalent concentrations to the leaching level (Supplementary Fig. 13). The surface area normalized kinetic rate constant for •OH

generation by FeOF was determined to be 31.7 μmol g L−1 min−1 m−2, 85.4 times higher than by FeOCl (Supplementary Table 4). Such increment closing to the •OH generation enhancement reveals

that the smaller particle size and higher surface area are not the primary factors. Consequently, we deduced that the disparity of H2O2 activation activity could be ascribed to the presence

of F-Fe-O sites, where the iron atom is expected to show much lower electron density over Cl-Fe-O. This capacity could be maintained at a wide pH range (3.0~9.0) since a relative steady •OH

generation was monitored and confirmed in Fig. 3D, demonstrating the surprising pH-adaptability of FeOF. In particular, the FeOF catalyst outperformed all the ever-reported heterogeneous

Fenton catalysts, showing a great •OH generation capacity (Fig. 3E and Supplementary Table 4). The neutral FeOF/H2O2 system also outperforms the traditional homogeneous Fenton process

initiated by Fe(II) ions at pH 3.0, regarding the produced •OH amount (353.0 μM _vs_ 280.1 μM) (Supplementary Fig. 14) and H2O2 utilization efficiency (Supplementary Table 5). Notably, the

H2O2 utilization efficiency toward selective •OH generation is found to be 33.2% at neutral condition, which is 1~3 orders of magnitude higher than other Fenton systems facilitated by the

state-of-the-art catalysts (Supplementary Table 5). It is also worthy mentioned that even at comparatively low H2O2 concentrations, such as 0.10, 0.50, 1.00, and 5.00 mM, the FeOF was still

capable to generate 8.2, 21.7, 48.4, and 98.0 μM of •OH respectively (Fig. 3F). Whereas, the counterpart FeOCl is hard to produce •OH from H2O2 selective decomposition at the equal

condition. Overall, it is clear that the FeOF demonstrates an excellent Fenton catalysis activity for efficient •OH generation with wide operation pH and high H2O2 utilization efficiency

(i.e., selectivity). This superior activity of FeOF for neutral Fenton process may be derived from the unique coordination configuration and electronic structure of iron sites mediated by

the fluoride atom with high electronegativity. FLUORINE COORDINATION DOMINATES H2O2 ACTIVATION ENHANCEMENT The Lewis acid-base interaction between catalysts and H2O2 is recognized as the

initial step and is of significant importance for H2O2 activation46. To clarify the role of Lewis acid sites (i.e., iron sites) within FeOF catalyst on H2O2 activation, we assessed the

effect of phosphate, a strong Lewis base for blocking interaction between iron sites and H2O2 molecules60, on •OH generation. As shown in Supplementary Fig. 15A, the phosphate addition

completely suppresses the •OH production confirmed by the no detection of 7-hydroxycoumarin (Supplementary Fig. 15B), demonstrating the unique catalysis role of iron sites for activating

H2O2 into •OH. Although our experimental findings suggested that FeOF had a somewhat higher Lewis acidity than FeOCl (~3× higher, Fig. 1F), this alone failed to explain the much higher

observed disparity in the accumulated generation of •OH (~168× higher). Even if we normalized the apparent kinetic rate constant for •OH generation by the total Lewis acidity (Supplementary

Table 4), the value for FeOF was 60 times greater than FeOCl. We observed that the ratio of Lewis acid sites with strong strength greatly increased from 1.9% to 44.9% as the fluorine

coordination was integrated. Meanwhile, the ratio of Lewis acid sites with medium strength also increased by more than 2 times, accompanied by the disappearance of weak-strength acid sites.

According to previous reports61,62,63, the type of Lewis acid site typically depends on the electron density of metal sites, which governs the interaction with Lewis bases. The observed

increased ratio of stronger acid sites verifies the electron-withdrawing function of fluorine coordination. Therefore, we attribute this significant enhancement to the function of fluorine

coordination, which optimizes the electronic structure of iron sites through the high electronegativity. We then further applied DFT calculations to comprehensively elucidate the interaction

between iron sites and H2O2 molecule at an atomic level. The interaction configuration is pivotal for digging the origin of Fenton catalysis performance improved by fluorine coordination.

By revealing the adsorption energy (Eb) and charge transfer, the ascendancy of F-Fe coordination on H2O2 activation can be clearly demonstrated. In this respect, we systematically calculated

these two depicters at four main facets, i.e., (101), (110), (211), and (010), in FeOF and FeOCl, which were extracted from the XRD patterns with high peak intensity. As illustrated in Fig.

 4A, B and Supplementary Fig. 16, the corresponding Eb of H2O2 on the Fe at all calculated facets of FeOF were determined to be −0.93, −0.84, −0.91, and −0.21 eV, respectively, which were

lower than those of FeOCl (i.e., −0.43, −0.06, −0.73, and −0.15 eV, respectively). This can be attributed to the stronger electron polarization effect of F over Cl. Notably, the length of

O-O bond (denoted as IO-O) within H2O2 molecule prolongs after adsorbing onto (110) and (211) facets of FeOF (Supplementary Table 6). The IO-O is also longer than that adsorbed onto the

facets in FeOCl, indicating the superior capacity of FeOF for H2O2 activation11,58,64,65. To unravel the electronic mechanism dominating the Fenton activity, we calculated the projected

density of state (PDOS) for both H2O2 before and after adsorption onto differing facets of FeOF and FeOCl. In addition, the charge density of H2O2-FeOF and H2O2-FeOCl complexes were also

investigated to elucidate the electron transfer over H2O2 and catalysts. It is apparent that the overall energy levels of H2O2 downshift to more negative positions after adsorbed to (101),

(110), and (211) facets of FeOF and all the screened facets of FeOCl (Supplementary Fig. 17). Specifically, the highest occupied molecular orbital (HOMO) of H2O2 is subjected to an obvious

splitting after being adsorbed to (101) facets of FeOF and FeOCl. However, new bands caused by splitting contribute slightly above the Fermi level despite of the occurrence of charge

depletion and accumulation. This indicated that H2O2 was inclined to be physically adsorbed onto (101) facets of both FeOF and FeOCl rather than to be chemically activated11,58. On the

contrary, the split HOMO of H2O2 adsorbed onto (110) and (211) facets (Supplementary Fig. 17) were partially unoccupied accompanying with the formation of new states beyond the Fermi level,

indicating the occurrence of chemisorption11,13,35. In particular, the molecular energy level of H2O2 adsorbed onto FeOF was much lower than that onto FeOCl. The calculated PDOS results

showed that the formed H2O2-FeOF complex on (110) and (211) facets after adsorption have a higher density state near the Fermi level as compared to the H2O2-FeOCl complex. Meanwhile, Bader

charge analysis revealed that O atoms in H2O2 contributed 0.10 _e_ to iron centers at both (110) and (211) facets of FeOCl while more charges (i.e., 0.15 and 0.18 _e_) transferred from O to

Fe atoms at corresponding facets of FeOF were evidently observed (Fig. 4C, D, and Supplementary Fig. 18). We noted that the charge depletion and accumulation detected in optimized

H2O2-catalyst geometry was highly consistent with the adsorption energies of H2O2 (Supplementary Table 6) on all facets of catalysts excluding the (010) facet (Supplementary Fig. 18). These

results manifested that FeOF exhibits a stronger activation capacity toward H2O2 than FeOCl via improved electron mobility, which can be ascribed to the robust electron polarization effect

of fluoride atoms. However, the facet-dependent catalytic performance of FeOF for H2O2 activation still needs to be further explored. The generation of •OH and intermediate species during

Fenton process were subsequently compared for FeOF and FeOCl. The •OH generation occurring on the various crystal surfaces of the catalyst includes H2O2 adsorption and consequent reactions.

The free energy diagram for the crystal surfaces of catalysts was optimized as following: * (i) → *H2O2 (ii) → *OH + •OH (iii) → *+2•OH (iv) (Fig. 4E, F), where * indicates the adsorption

state. The changes in the free energies for •OH formation in (211), (110), (101), and (010) facets of FeOF and FeOCl are displayed in Fig. 4E, F, and Supplementary Figs. 19–21. The

coordination environment evolutions of corresponding iron sites are presented in the caption. The H2O2 adsorption (ii) was observed as the rate-limiting step for all facets due to the

highest energy barrier. Notably, H2O2 adsorption on FeOF catalyst showed much lower free energy than FeOCl for (211), (110), and (101) facets, indicating the easier access of iron centers

coordinated with fluoride atoms. Therefore, H2O2 adsorption to FeOF was thermodynamically more favorable than to FeOCl. Subsequently, the H2O2 on catalyst surface initiated to exothermically

split into *OH accompanying with one •OH desorption (iii) followed by the dissociation of another •OH (iv) (Fig. 4E). The energy barriers requiring for H2O2 split and •OH desorption on the

(211) (−2.87 eV), (110) (−2.54 eV), and (101) (−2.45 eV) facets of FeOF were found to be much lower than those of FeOCl (Supplementary Table 7), demonstrating the superior activity of FeOF

for H2O2 activation. Of note, although H2O2 adsorption to (010) facets of FeOF and FeOCl show a similar free energy value (ca. 0.9 eV), the following split reaction demonstrated a relative

higher activation energy barrier over (211), (110), and (101) facets (Supplementary Fig. 21), suggesting the inferior catalytic performance of (010) facets. Interestingly, the

rate-determining step (i.e., H2O2 adsorption) in calculated facets (>0 eV) was endothermic except the (211) (−0.14 eV) facet of FeOF (Fig. 4F and Supplementary Table 7). Theoretically,

the catalyst with the lowest free energy in rate-limiting step would show optimum activity for Fenton reactions58,65. It is therefore expected that the (211) facet of FeOF outperforms the

additional facets in terms of H2O2 activation due to the exothermic nature of H2O2 adsorption following by the spontaneous decomposition14,58. We conducted ab initio molecular dynamics (MD)

simulations to further unveil the evolution and fate of H2O2, detailed in Supplementary Fig. 22. H2O2 adsorbed on FeOF could be readily cleaved into two •OH radicals without energy barriers

to overcome. Conversely, the adsorbed H2O2 on FeOCl cannot split into •OH radicals. The divergence in H2O2 split performance between FeOF and FeOCl further highlights the unique function of

fluorine coordination. Overall, by changing the coordination environmental of iron centers with more electronegative fluoride atoms, the Fenton activity could be largely improved through

optimizing the energy barrier for H2O2 adsorption and subsequent splitting reactions. As electron transfer is responsible for H2O2 activation, we measured the Tafel polarization curves,

linear sweep voltammetry (LSV) plots, and electrochemical impedance spectroscopy (EIS), to detect real electron mitigation property of FeOF in Fenton process using electrochemical methods60.

According to the Tafel polarization curves (Supplementary Fig. 23), the corrosion current values were determined to be 8.49 × 10–7 and 1.640 × 10–8 A while the corrosion current densities

reached to 4.33 and 0.08 µA cm−2 for FeOF and FeOCl, respectively. The large difference of corrosion current values and densities imply that FeOF exhibited a superior electron transfer

performance and catalytic reactivity than FeOCl toward H2O2 activation. The LSV plot of FeOF (Supplementary Fig. 24) presented distinctly larger current density over the analogy, further

confirming the faster electron migration between FeOF and H2O2 for a rapid •OH generation and enhanced Fenton reaction. In addition, the relative lower arc radius observed in the EIS

spectrum (Supplementary Fig. 25) of FeOF catalyst matches well with the findings of Tafel polarization curves and LSV plots. These results experimentally elucidate that the electronic

structure engineering of active iron sites via coordinatively bonding fluoride atoms with the highest electronegativity significantly can promote the electron migration for the enhanced •OH

generation, which shows promising Fenton catalysis activity for potential applications. PERFORMANCE OF FEOF/H2O2 SYSTEM FOR PRACTICAL WATER PURIFICATION The requirement of acid environment

(pH 3.0~4.0) for H2O2 activation often causes undesirable complexity and difficulty, largely retarding the practicality of Fenton process9,30. Attributed to the unique fluorine coordination,

the FeOF catalyst can easily trigger H2O2 decomposition into abundant •OH at wide pH range, which is expected to tremendously facilitate the water purification applications for different

treating purposes. As a concept of proof, we examined the degradation efficiency of FeOF/H2O2 system using p-nitrophenol (4-NP), a refractory organic pollutant to ROS (e.g., 1O2 and ·O2−)

with moderate oxidation capacity, as the model substrate. The degradation of 4-NP as a function of time during Fenton reaction is illustrated in Fig. 5A. The FeOCl/H2O2 system could only

remove about 6.2% of 4-NP under current conditions. The 4-NP decomposition rate reaches ~100% at pH 7.0 accompanying a total organic carbon (TOC) removal of 63% (Supplementary Fig. 26)

within a short period (~30 min) at a pseudo-first-order rate constant (_k_obs) of 0.362 min−1 (Fig. 5B), which was 19.0 and 12.5 times higher compared to FeOCl (0.019 min−1) and the

conventional ferrihydrite (0.029 min−1) catalyst, being one of the most active Fe-based catalysts for H2O2 activation so far (Supplementary Table 4). However, 4-NP can be hardly removed by

individual H2O2 (Supplementary Fig. 27), FeOF alone (Supplementary Fig. 28) or leaching iron ions (Supplementary Fig. 29) at neutral condition. In particular, the FeOF/H2O2 system shows

similar performance to the typical homogeneous Fenton process (pH 3.0) initiated by Fe2+ ions with the equivalent dosage (Supplementary Fig. 30). We also observed that less than 0.40 mg L−1

of fluoride leached during Fenton reaction (Supplementary Fig. 31), which conformed to the drinking water standards issued by the United States of America (2.00 mg L−1), World Health

Organization (1.00 mg L−1), and China (1.00 mg L−1). Considering the possibility that empty orbitals of unsaturated iron centers in FeOF play a decisive role in H2O2 activation, we also

attempted to block the orbital via a Lewis acid-base interaction using phosphate. Similar to •OH generation inhibition, we observed a strong suppression of 4-NP decay with almost zero

percent degradation rate (Fig. 5C), suggesting that unsaturated iron centers (e.g., F-(Fe(III)O3)-F moiety) is responsible for 4-NP destruction. Moreover, we also observed that both methanol

and tert-butanol, two representative scavengers for •OH, showcased a severe inhibition effect in 4-NP removal at an excessive dosage (Supplementary Fig. 32). The residual 4-NP decomposition

rate (~1.0%) is probably attributed to the marginal adsorption capability of FeOF. In particular, the 4-NP decomposition rate showed an evident decline from 95.4% to 28.1% (Fig. 5C) in the

presence of TBA at a relatively lower concentration (i.e., 10 mM). The equal addition of MeOH retarded 70.6% of 4-NP being degraded by FeOF/H2O2 system, which was about 2.3% higher than TBA

inhibition, highlighting the slight contribution of surface-bound •OH radicals for 4-NP degradation. The contribution of free and surface-bound •OH radicals were quantified and calculated

according to previous study using the _k_obs value before and after quenching58. Specifically, the free and surface-bound •OH radicals account for 94.3% and 3.5% of the contributions (Fig. 

5D) to the neutral Fenton process initiated by FeOF catalyst. The inhibition results manifested that both the free and surface-bound •OH are generally produced via Fenton reaction, which

matched well with our observations in EPR and •OH probing results. The relationship between the Fenton degradation activity and reaction parameters, (e.g., pH value, temperature, and H2O2

dosage) was also investigated. Increasing pH values from 3.0 to 9.0 moderately impeded the 4-NP decay (Fig. 5E). This phenomenon was attributed to the relatively low redox potential of

formed •OH under alkaline conditions. Nevertheless, the _k_obs underwent a slight decrement with over 90% decomposition rate of 4-NP as pH increased to 9.0. Given the pH-adaptive Fenton

performance of FeOF/H2O2 system, the long-lasting challenge to produce •OH at a wide pH for applications, especially at neutral condition that closes to most of realistic scenarios, could be

easily addressed via the polarization of electron distribution over iron sites with fluorine coordination. Unlike pH impacts, the 4-NP degradation efficiency was largely enhanced when

increasing either the temperature (Supplementary Fig. 34) or H2O2 dosage (Supplementary Fig. 35). Specifically, a significant reduction of time to destruct 100% 4-NP (20 mg L−1) was observed

as 20 mmol L−1 of H2O2 or 40 °C of temperature was applied. The 4-NP could be also quickly removed at a lower H2O2 concentration (e.g., 1.00 mM), suggesting the strong ability of FeOF to

activate trace H2O2 for effective water decontaminations (Supplementary Fig. 35). We also observed that the FeOF/H2O2 system maintained satisfactory degradation capacity for successive seven

times running (Fig. 5F) without adding H2O2 each time. The degradation efficiency could be recovered once H2O2 is supplemented, suggesting the excellent stability and reusability of FeOF

catalyst. Similarly, successive recycle tests (Supplementary Fig. 36) with the addition of both 4-NP and H2O2 strongly indicated a self-enhanced activity feature of FeOF, which is an

indicative of the formation of Fe(II). We further performed XPS, Mössbauer, and electrochemical measurements to support the speculation of Fe(II) formation (Supplementary Figs. 

37–39)53,54,66. The results suggested that ~26.5% of Fe(II) was generated after Fenton process, which substantially facilitated the cycling of Fe(III)/Fe(II) redox as well as the degradation

efficiency for 4-NP. The observation of higher open-circuit potential of Fe(III) in FeOF and smaller peak-to-peak separation (ΔEp) (from 0.40 V to 0.28 V) depicted in Supplementary Fig. 39

indicated the more facile reversibility of the Fe(III)/Fe(II) cycle of FeOF with fluorine coordination67,68,69. Besides, we also found that the proportion of leaching Fe2+ ions increased

from 3% to 42% (Supplementary Fig. 39B), further evidencing the enhancement of Fe(III)/Fe(II) redox cycle. Note that sodium chloride (NaCl) is commonly presented at various industrial

wastewaters and proposed as a major interference for Fenton process with undesirable side effects. We did not observe any marginal deterioration in 4-NP decay (Supplementary Fig. 40) even at

a concentration as high as 5.0 g L−1, demonstrating the FeOF/H2O2 system shows great potential in purifying high salinity wastewaters. We further screened a broad spectrum of organic

pollutants with high recalcitrance, such as dyes and antibiotics that have wide industrial and pharmaceutical applications, to investigate the versatility of FeOF/H2O2 system. As shown in

Fig. 5G, FeOF is efficient to degrade all the model organics applied with a _k_obs (Supplementary Fig. 41) in a range of 0.19~0.41 min−1 (Supplementary Fig. 42). Moreover, we observed that

FeOF could inactivate 99.8% of a model microorganism _E.coli_ (Supplementary Fig. 43), whereas the control system (6.8% for H2O2 only) exhibited a marginal antibacterial activity,

demonstrating its superiority in bacterial deactivation. Together with the high reactivity, the as-prepared FeOF catalyst can be operated at more adaptive pH range than the state-of-the-art

Fenton catalysts. It is suggested that there is no need to adjust the pH value of target wastewaters, further simplifying the overall operation process and lowering the net cost as well. To

this end, we collected several secondary effluents from pharmaceutical and textile industries for testing the practicality of FeOF/H2O2 system without pH adjustment. Indicated by the

observation in excitation-emission matrix (EEM) spectra (Fig. 5H, I), soluble microbial byproducts and humic acid-like organics presented in these effluents were easily removed with

evidencing by the significant decrease of fluorescence intensity at detected peaks70,71. A moderate TOC removal (up to 50.5%) (Supplementary Fig. 44) was found after treating the collected

effluents by FeOF/H2O2 system while the pH suffered a slightly increase to ~8.0 (Supplementary Fig. 45). Noting that the TOC removal is influenced by the specific content of organic

pollutants in wastewater streams and could be facilely adjusted by increasing the input of H2O2. The results of tentative attempts highlighted that the rationally designed FeOF with unique

fluorine coordination could reform the chemical-intensive water treatment process for broad applications with high feasibility. DISCUSSION In summary, we demonstrated a perspective for

understanding the Fenton catalysis by the electronic structure modulation of iron sites with unique fluorine coordination. Sufficient evidence suggested that the coordinated fluorine atom

featuring the most electronegativity could largely reduce the local electron density of iron sites, thereby facilitating H2O2 activation through lowering the energy barriers of the

rate-limiting H2O2 adsorption step and subsequent O-O bond splitting reactions. As a result, the rationally designed FeOF exhibited an extraordinary Fenton activity for efficient •OH

generation in terms of quantity (up to 450 μM) and selectivity (33.2%), significantly outperforming FeOCl analogy and the state-of-the-art Fenton catalysts ever recorded. Moreover, the

enhanced interaction between iron sites and H2O2 molecules endowed FeOF with high pH-adaptability, thus breaking the limitations of harsh operation pH condition. The established FeOF/H2O2

system shows great practical potential for water purification as it is highly efficient to degrade various recalcitrant pollutants as well as to decontaminate different wastewaters. To

balance the •OH production and utilization, further studies should be conducted to integrate the FeOF catalyst with the nanoconfined space for maximizing the practice potential. This work

provides a significant insight into the electronic structure modulation of active sites with fluorine coordination at the atomic scale, which affords a rational design principle for

developing advanced Fenton catalysts that effectively and selectively activate H2O2 into •OH radicals. METHODS MATERIALS All chemicals and materials are analytically pure or higher and

directly used without further purification (Supplementary Note 1). Ultrapure water from a Milli-Q system (_R_ > 18 MΩ) was used for all experiments. CATALYST PREPARATION A two-step

reaction was conducted to synthesize FeOF catalyst according to previous work36 with modification. Typically, the precursor FeSiF6•6H2O was first prepared by adding iron powder (10.0 g) into

fluorosilicic acid solution (100 mL) with vigorous stirring at 50 °C for 12 h. Note that the reaction should be carefully carried out at a Teflon breaker. The resultant solution was then

suffered vacuum filtration to remove residual iron powder. After drying at 60 °C for 24 h, a blue crystalline solid of FeSiF6•6H2O was collected and restored for usage. In the second step,

1.0 g of the as-prepared FeSiF6•6H2O precursor was mixed with 150 mL of n-propanol stirred for 30 min. The mixture was then transferred into a 200 mL Teflon-lined autoclave and heated at 200

 °C for 10 h to complete the solvothermal reaction. After being naturally cooled to room temperature, the product was centrifuged, washed with ethanol, and vacuum-dried at 80 °C for 24 h.

The synthesis of FeOCl catalyst was referring to Sun et al.’s work9 and detailed in Supplementary Note 1. CHARACTERIZATION METHODS The crystal structures of the catalysts were assessed by

powder XRD with a Thermo Scientific ARL-XTRA X-ray diffractometer. The microscopic morphologies were observed using a field-emission scanning electron microscope (SEM, Zeiss Ultra 55) and

transmission electron microscope (TEM, TalosF200X). The HAADF-STEM images were recorded with an FEI Themis Z scanning transmission electron microscope with double aberration correctors in

STEM mode (Super-X EDS). XPS (Thermo Scientific K-Alpha) was performed to analyze the surface elemental compositions and chemical states of the catalysts. The Lewis acid sites were analyzed

by in situ pyridine-chemosorbed Fourier Transform-Infrared Spectroscopy (Py-IR, Thermo Scientific Nicolet iS10), and the measurement details were provided in Supplementary Note 2. The 57Fe

Mössbauer spectroscopy (Topologic 500 A) technique was performed to unravel the coordination environment of iron sites in the catalysts before and after application under room temperature

using 57Co (Rh) λ-ray as irradiation source. The XAFS spectra of the Fe K-edge were recorded at the Singapore Synchrotron Radiation Light Source. The electrochemical performances were

measured on a CHI 660E workstation (CH Instruments) with a three-electrode cell. The leaching concentrations of iron ions in Fenton reaction solutions were measured by ICP-MS (Agilent

720ES). THEORETICAL CALCULATIONS All theoretical calculations based on the DFT were performed using Vienna ab initio simulation package (VASP) within the generalized gradient approximation

using the Perdew–Burke–Ernzerhof functional72,73. Detailed information is shown in Supplementary Note 3. EXPERIMENT PROCEDURES All the experiments were carried out in a 100-ml beaker at 20 ±

 2 °C using a shaker incubator. The initial pH values of the solutions were adjusted with 0.1 M HCl or 0.1 M NaOH. For Fenton activity evaluation, the accumulated •OH generation

concentration of established Fenton systems with various catalysts (0.1 g L−1) was evaluated using coumarin (10 mM) as the selective probe. For pollutant degradation assessment, a certain

amount of the catalyst was added to 50 mL 4-NP (20 mg L−1) and was dispersed uniformly using ultrasonication for 1 min. Then, a given volume of H2O2 was added to the suspension to initiate

the Fenton reaction. At the specified time intervals, a 2.0-mL sample was withdrawn, filtered through a polyether sulfone membrane (0.22 µm), and immediately quenched using TBA before

analysis. For the •OH scavenging experiment, MeOH (10 mM) and TBA (10 mM) were used to quench •OH (i.e., •OHf and •OHsurf) and •OHf radicals, respectively74. The cyclic experiments (with or

without adding H2O2), Fe leaching experiments, coexisting ion (i.e., Cl−) experiments, pH (i.e., 3.0, 4.0, 5.0, 6.0, 7.0, 8.0, and 9.0) experiments, H2O2 dosage (1.0, 5.0, 10.0, 15.0, and

20.0 mM) experiments, temperature experiments (i.e., 20, 30, and 40 °C), contaminants (i.e., tetracycline, atrazine, sulfamethoxazole, ofloxacin, and salicylic acid) experiments, and

industrial effluents experiments were conducted to explore the practical considerations of pH-adaptive FeOF/H2O2 Fenton system. All the experiments were performed three times to ensure

reproducibility. ANALYTIC METHODS The •OH radicals were quantified using a fluorescence method with coumarin as the probe, which could be converted into 7-hydroxycoumarin (7-HC) with 29%

selectivity59. Further details for •OH measurement and quantification are provided in Supplementary Note 4. The concentrations of the contaminants were determined by high-performance liquid

chromatography (Agilent 1260) with DAD detector and ZORBAX Eclipse XDB-C18 column (4.6 × 150 mm, 3.5 μm) at the corresponding detection wavelengths. The H2O2 concentration was determined by

a titanium (IV) spectrophotometric method75. The presence of •OH was identified by an EPR spectrometer (Bruker A300) using DMPO as the trapping agent65. TOC was measured on an Elementar

liquiTOC II Total Organic Carbon analyzer. The graphs with error bars are presented with standard deviation of the experiment in triplicate. REPORTING SUMMARY Further information on research

design is available in the Nature Portfolio Reporting Summary linked to this article. DATA AVAILABILITY The data generated in this study are provided with in the article and the

Supplementary Information file. Source data are provided with this paper. REFERENCES * Greve, P. et al. Global assessment of water challenges under uncertainty in water scarcity projections.

_Nat. Sustain._ 1, 486–494 (2018). Article  Google Scholar  * Mekonnen, M. M. et al. Four billion people facing severe water scarcity. _Sci. Adv._ 2, e1500323 (2016). Article  ADS  PubMed 

PubMed Central  Google Scholar  * Guo, Z.-Y. et al. Electron delocalization triggers nonradical Fenton-like catalysis over spinel oxides. _Proc. Natl Acad. Sci. USA_ 119, e2201607119 (2022).

Article  CAS  PubMed  PubMed Central  Google Scholar  * Xu, N. et al. Going beyond efficiency for solar evaporation. _Nat. Water_ 1, 494–501 (2023). Article  Google Scholar  * dos Santos,

A. J. et al. Accelerating innovative water treatment in Latin America. _Nat. Sustain._ 6, 349–351 (2023). Article  Google Scholar  * He, C. et al. Future global urban water scarcity and

potential solutions. _Nat. Commun._ 12, 4667 (2021). Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  * Zhang, Y.-J. et al. Distinguishing homogeneous advanced oxidation processes

in bulk water from heterogeneous surface reactions in organic oxidation. _Proc. Natl Acad. Sci. USA_ 120, e2302407120 (2023). Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  *

Hodges, B. C. et al. Challenges and prospects of advanced oxidation water treatment processes using catalytic nanomaterials. _Nat. Nanotechnol._ 13, 642–650 (2018). Article  ADS  CAS  PubMed

  Google Scholar  * Sun, M. et al. Reinventing fenton chemistry: iron oxychloride nanosheet for pH-insensitive H2O2 activation. _Environ. Sci. Technol. Lett._ 5, 186–191 (2018). Article  CAS

  Google Scholar  * Chen, Z. et al. Single-atom Mo-Co catalyst with low biotoxicity for sustainable degradation of high-ionization-potential organic pollutants. _Proc. Natl Acad. Sci. USA_

120, e2305933120 (2023). Article  CAS  PubMed  PubMed Central  Google Scholar  * Zhan, H. et al. Selective hydroxyl generation for efficient pollutant degradation by electronic structure

modulation at Fe sites. _Proc. Natl Acad. Sci. USA_ 120, e2305378120 (2023). Article  PubMed  PubMed Central  Google Scholar  * Xing, M. et al. Metal sulfides as excellent co-catalysts for

H2O2 decomposition in advanced oxidation processes. _Chem_ 4, 1359–1372 (2018). Article  CAS  Google Scholar  * Xiong, Y. et al. Single-atom Fe catalysts for Fenton-like reactions: roles of

different N species. _Adv. Mater._ 34, 2110653 (2022). Article  CAS  Google Scholar  * Zhang, D. et al. Dynamic active-site induced by host-guest interactions boost the Fenton-like reaction

for organic wastewater treatment. _Nat. Commun._ 14, 3538–3538 (2023). Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  * Wang, J. et al. Sustainable and feasible reagent-free

electro-Fenton via sequential dual-cathode electrocatalysis. _Proc. Natl Acad. Sci. USA_ 118, e2108573118 (2021). Article  CAS  PubMed  PubMed Central  Google Scholar  * Yan, Q. et al.

Constructing an acidic microenvironment by MoS2 in heterogeneous Fenton reaction for pollutant control. _Angew. Chem. Int. Ed._ 60, 17155–17163 (2021). Article  CAS  Google Scholar  * Su, L.

et al. Regulating local electron density of iron single sites by introducing nitrogen vacancies for efficient photo-fenton process. _Angew. Chem. Int. Ed._ 60, 21261–21266 (2021). Article 

CAS  Google Scholar  * Zhou, X. et al. Identification of Fenton-like active Cu sites by heteroatom modulation of electronic density. _Proc. Natl Acad. Sci. USA_ 119, e2119492119 (2022).

Article  CAS  PubMed  PubMed Central  Google Scholar  * Wu, L. et al. Preferential growth of the cobalt (200) facet in Co@N-C for enhanced performance in a Fenton-like reaction. _ACS Catal._

11, 5532–5543 (2021). Article  ADS  CAS  Google Scholar  * Duong, D. L. et al. Van der Waals layered materials: opportunities and challenges. _ACS Nano_ 11, 11803–11830 (2017). Article  CAS

  PubMed  Google Scholar  * Tanaka, Y. et al. New oxyhalide solid electrolytes with high lithium ionic conductivity >10 mS cm−1 for all-solid-state batteries. _Angew. Chem. Int. Ed._ 62,

e202217581 (2023). Article  CAS  Google Scholar  * Suresh, R. et al. Halides and oxyhalides-based photocatalysts for abatement of organic water contaminants - An overview. _Environ. Res._

212, 113149 (2022). Article  CAS  PubMed  Google Scholar  * de Arquer, F. P. G. et al. 2D metal oxyhalide-derived catalysts for efficient CO2 electroreduction. _Adv. Mater._ 30, 1802858

(2018). Article  Google Scholar  * Zeng, Y. et al. 2D FeOCl: a highly in-plane anisotropic antiferromagnetic semiconductor synthesized via temperature-oscillation chemical vapor transport.

_Adv. Mater._ 34, 2108847 (2022). Article  CAS  Google Scholar  * Yang, X.-j et al. Iron oxychloride (FeOCl): an efficient Fenton-like catalyst for producing hydroxyl radicals in degradation

of organic contaminants. _J. Am. Chem. Soc._ 135, 16058–16061 (2013). Article  CAS  PubMed  Google Scholar  * Ji, X.-X. et al. First principles study of Fenton reaction catalyzed by FeOCl:

reaction mechanism and location of active site. _Rare Met._ 38, 783–792 (2019). Article  CAS  Google Scholar  * Ding, Y. et al. Regulating interlayer confinement FeOCl for accelerating

polymerization of pollutants to reduce carbon emission in water purification. _ACS Appl. Mat. Interfaces_ 15, 5058–5070 (2023). Article  CAS  Google Scholar  * Cui, L. et al. Overcoming the

activity-stability trade-off in heterogeneous electro-fenton catalysis: encapsulating carbon cloth-supported iron oxychloride within graphitic layers. _ACS Catal._ 12, 13334–13348 (2022).

Article  CAS  Google Scholar  * Sun, M. et al. Reactive, self-cleaning ultrafiltration membrane functionalized with iron oxychloride nanocatalysts. _Environ. Sci. Technol._ 52, 8674–8683

(2018). Article  ADS  CAS  PubMed  Google Scholar  * Wang, J. et al. Interlayer structure manipulation of iron oxychloride by potassium cation intercalation to steer H2O2 activation pathway.

_J. Am. Chem. Soc._ 144, 4294–4299 (2022). Article  CAS  PubMed  Google Scholar  * Shang, Y. et al. Single-atom catalysis in advanced oxidation processes for environmental remediation.

_Chem. Soc. Rev._ 50, 5281–5322 (2021). Article  CAS  PubMed  Google Scholar  * Zhu, Y. et al. Strategies for enhancing the heterogeneous Fenton catalytic reactivity: a review. _Appl. Catal.

B Environ._ 255, 117739 (2019). Article  CAS  Google Scholar  * Zhang, J., Shan, C., Zhang, W. & Pan, B. In situ ligand-modulated activation of inert Ce(III/IV) into ozonation catalyst

for efficient water treatment. _Proc. Natl Acad. Sci. USA_ 120, e2305255120 (2023). Article  CAS  PubMed  PubMed Central  Google Scholar  * Wang, B. et al. A site distance effect induced by

reactant molecule matchup in single-atom catalysts for Fenton-like reactions. _Angew. Chem. Int. Ed._ 61, 202207268 (2022). Article  ADS  Google Scholar  * Wu, Q.-Y. et al. Oxygen doping of

cobalt-single-atom coordination enhances peroxymonosulfate activation and high-valent cobalt-oxo species formation. _Proc. Natl Acad. Sci. USA_ 120, e2219923120 (2023). Article  CAS  PubMed

  PubMed Central  Google Scholar  * Pereira, N. et al. Iron oxyfluorides as high capacity cathode materials for lithium batteries. _J. Electrochem. Soc._ 156, A407–A416 (2009). Article  CAS

  Google Scholar  * Park, M. et al. FeOF ellipsoidal nanoparticles anchored on reduced graphene oxides as a cathode material for sodium-ion batteries. _J. Power Sources_ 396, 551–558 (2018).

Article  ADS  CAS  Google Scholar  * Yao, L. et al. Direct observation of oxygen vacancy-driven structural and resistive phase transitions in La2/3Sr1/3MnO3. _Nat. Commun._ 8, 14544 (2017).

Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  * Li, W. et al. FeOF/TiO2 hetero-nanostructures for high-areal-capacity fluoride cathodes. _ACS Appl. Mat. Interfaces_ 12,

33803–33809 (2020). Article  CAS  Google Scholar  * Yun, B. et al. The effect of Ni doping on FeOF cathode material for high-performance sodium-ion batteries. _Small_

https://doi.org/10.1002/smll.202308011 (2023). * Wan, X. et al. Iron atom-cluster interactions increase activity and improve durability in Fe-N-C fuel cells. _Nat. Commun._ 13, 2963 (2022).

Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  * Li, H. et al. Wavelength-dependent differences in photocatalytic performance between BiOBr nanosheets with dominant exposed (001)

and (010) facets. _Appl. Catal. B Environ._ 187, 342–349 (2016). Article  CAS  Google Scholar  * Liang, H. et al. Synergistic effect of dual sites on bimetal-organic frameworks for highly

efficient peroxide activation. _J. Hazard. Mater._ 406, 124692 (2021). Article  CAS  PubMed  Google Scholar  * Zarate, X., Schott, E. & Arratia-Perez, R. Effects of the peripheral

substituents (-NH2, -OH, -CH3, -H, -C6H5, -Cl, -CO2H and -NO2) on molecular properties of a Ni-Porphyrazine dimers family. _Polyhedron_ 50, 131–138 (2013). Article  CAS  Google Scholar  * M.

Thommes et al. Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report). _Pure Appl. Chem._ 87, 1051–1069 (2015).

* Mo, F. et al. The optimized Fenton- like activity of Fe single- atom sites by Fe atomic clusters-mediated electronic configuration modulation. _Proc. Natl Acad. Sci. USA_ 120, e2300281120

(2023). Article  CAS  PubMed  PubMed Central  Google Scholar  * Xia, H. et al. Catalytic conversion of glucose to 5-hydroxymethyfural over Fe/β zeolites with extra-framework isolated Fe

species in a biphasic reaction system. _Biomass Bioenergy_ 108, 426–432 (2018). Article  CAS  Google Scholar  * Jia, Z. et al. Hollow nano-MgF2 supported catalysts: Highly active and stable

in gas-phase dehydrofluorination of 1,1,1,3,3-pentafluoropropane. _Appl. Catal. B Environ._ 238, 599–608 (2018). Article  CAS  Google Scholar  * Wang, H. et al. Modulating inherent lewis

acidity at the intergrowth interface of mortise-tenon zeolite catalyst. _Nat. Commun._ 13, 2924 (2022). Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  * Emeis, C. A.

Determination of integrated molar extinction coefficients for IR absorption bands of pyridine adsorbed on solid acid catalysts. _J. Catal._ 141, 347–354 (1993). Article  CAS  Google Scholar

  * Yang, T. et al. Accelerating Fe(III)/Fe(II) cycle via Fe(II) substitution for enhancing Fenton-like performance of Fe-MOFs. _Appl. Catal. B Environ._ 286, 119859 (2021). Article  CAS 

Google Scholar  * L. Duan et al. Defective iron based metal-organic frameworks derived from zero-valent iron for highly efficient Fenton-like catalysis. _J. Hazard. Mater_. 445, 130426

(2023). * Yang, G. et al. Regulating Fe-spin state by atomically dispersed Mn-N in Fe-N-C catalysts with high oxygen reduction activity. _Nat. Commun._ 12, 1734 (2021). Article  ADS  CAS 

PubMed  PubMed Central  Google Scholar  * Kim, D. H. et al. Selective electrochemical reduction of nitric oxide to hydroxylamine by atomically dispersed iron catalyst. _Nat. Commun._ 12,

1856 (2021). Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  * Pan, Y. et al. Regulating the coordination structure of single-atom Fe-NxCy catalytic sites for benzene oxidation.

_Nat. Commun._ 10, 4290 (2019). Article  ADS  PubMed  PubMed Central  Google Scholar  * Xu, X. et al. Identifying the role of surface hydroxyl on FeOCl in bridging electron transfer toward

efficient persulfate activation. _Environ. Sci. Technol._ 57, 12922–12930 (2023). Article  ADS  CAS  PubMed  Google Scholar  * Zhou, Q. et al. Generating dual-active species by triple-atom

sites through peroxymonosulfate activation for treating micropollutants in complex water. _Proc. Natl Acad. Sci. USA_ 120, e2300085120 (2023). Article  CAS  PubMed  PubMed Central  Google

Scholar  * Xu, X. et al. Revealing *OOH key intermediates and regulating H2O2 photoactivation by surface relaxation of Fenton-like catalysts. _Proc. Natl Acad. Sci. USA_ 119, e2205562119

(2022). Article  CAS  PubMed  PubMed Central  Google Scholar  * Tokumura, M. et al. Iron redox cycling in hydroxyl radical generation during the photo-Fenton oxidative degradation: dynamic

change of hydroxyl radical concentration. _Appl. Catal. B Environ._ 106, 565–576 (2011). Article  CAS  Google Scholar  * Gao, C. et al. Enhanced Fenton-like catalysis by iron-based metal

organic frameworks for degradation of organic pollutants. _J. Catal._ 356, 125–132 (2017). Article  CAS  Google Scholar  * Brown, I. D. et al. Electronegativity and Lewis acid strength. _J.

Am. Chem. Soc._ 112, 3401–3403 (1990). Article  CAS  Google Scholar  * Lawrence, A. S. et al. Detecting Lewis acid sites in metal-organic frameworks by density functional theory. _Mol.

Catal._ 517, 112042 (2022). Article  CAS  Google Scholar  * Yang, Q. et al. Atomically dispersed Lewis acid sites boost 2-electron oxygen reduction activity of carbon-based catalysts. _Nat.

Commun._ 11, 5478 (2020). Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  * F. Li et al. Efficient photo-Fenton reaction for tetracycline and antibiotic resistant bacteria removal

using hollow Fe-doped In2O3 nanotubes: from theoretical research to practical application. _Water Res_. 240, 120088 (2023). * Jiang, Y. et al. In situ turning defects of exfoliated Ti3C2

MXene into Fenton-like catalytic active sites. _Proc. Natl Acad. Sci. USA_ 120, e2210211120 (2022). Article  PubMed  PubMed Central  Google Scholar  * Wang, C. et al. Accelerating

Fe(III)/Fe(II) redox cycling in heterogeneous electro-Fenton process via S/Cu-mediated electron donor-shuttle regime. _Appl. Catal. B Environ. Energ._ 342, 123457 (2024). Article  CAS 

Google Scholar  * Mei, S.-C. et al. Heterogeneous Fenton water purification catalyzed by iron phosphide (FeP). _Water Res._ 241, 120151–120151 (2023). Article  CAS  PubMed  Google Scholar  *

Liu, M. et al. Accelerated Fe2+ regeneration in an effective electro-fenton process by boosting internal electron transfer to a nitrogen-conjugated Fe(III) complex. _Environ. Sci. Technol._

55, 6042–6051 (2021). Article  ADS  CAS  PubMed  Google Scholar  * Tan, W. et al. Peroxymonosulfate activated with waste battery-based Mn-Fe oxides for pollutant removal: electron transfer

mechanism, selective oxidation and LFER analysis. _Chem. Eng. J._ 394, 124864 (2020). Article  CAS  Google Scholar  * Hu, Q. et al. Unraveling timescale-dependent Fe-MOFs crystal evolution

for catalytic ozonation reactivity modulation. _J. Hazard. Mater._ 431, 128575 (2022). Article  CAS  PubMed  Google Scholar  * Q. Hu et al., Promoting •OH-dominant Fenton-like process over

peracetic acid activation by ultrafine FeOx nanoclusters anchored carbonaceous nanosheets. _Fundam. Res._ https://doi.org/10.1016/j.fmre.2023.05.007 (2023). * Perdew, J. P., Burke, K. &

Ernzerhof, M. Generalized gradient approximation made simple. _Phys. Rev. Lett._ 77, 3865–3868 (1996). Article  ADS  CAS  PubMed  Google Scholar  * Kresse, G. & Joubert, D. From

ultrasoft pseudopotentials to the projector augmented-wave method. _Phys. Rev. B_ 59, 1758–1775 (1999). Article  ADS  CAS  Google Scholar  * Li, M. et al. Single cobalt atoms anchored on

Ti3C2Tx with dual reaction sites for efficient adsorption-degradation of antibiotic resistance genes. _Proc. Natl Acad. Sci. USA_ 120, e2305705120 (2023). Article  CAS  PubMed  PubMed

Central  Google Scholar  * Yang, Z., Qian, J., Yu, A. & Pan, B. Singlet oxygen mediated iron-based Fenton-like catalysis under nanoconfinement. _Proc. Natl Acad. Sci. USA_ 116, 6659–6664

(2019). Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  Download references ACKNOWLEDGEMENTS This work was supported by the National Natural Science Foundation of China

(22106141, D.Y. and 22176124, J.L.), China Postdoctoral Science Foundation (2022M712827, D.Y.), Research Start-up Funding from Shanghai Jiao Tong University (WH220416002, J.L.), and

Fundamental Research Funds of Zhejiang Sci-Tech University (23202131-Y, D.Y.). AUTHOR INFORMATION Author notes * These authors contributed equally: Deyou Yu, Licong Xu. AUTHORS AND

AFFILIATIONS * Engineering Research Center for Eco-Dyeing and Finishing of Textiles (Ministry of Education), Zhejiang Sci-Tech University, Hangzhou, 310018, PR China Deyou Yu, Licong Xu, 

Shanli Wang & Minghua Wu * School of Environmental Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China Kaixing Fu, Chunyu Lv & Jinming Luo * College of

Chemistry and Chemical Engineering, Qingdao University, Qingdao, 266071, PR China Xia Liu * School of Material Science & Engineering, Zhejiang Sci-Tech University, Hangzhou, 310018, PR

China Wangyang Lu Authors * Deyou Yu View author publications You can also search for this author inPubMed Google Scholar * Licong Xu View author publications You can also search for this

author inPubMed Google Scholar * Kaixing Fu View author publications You can also search for this author inPubMed Google Scholar * Xia Liu View author publications You can also search for

this author inPubMed Google Scholar * Shanli Wang View author publications You can also search for this author inPubMed Google Scholar * Minghua Wu View author publications You can also

search for this author inPubMed Google Scholar * Wangyang Lu View author publications You can also search for this author inPubMed Google Scholar * Chunyu Lv View author publications You can

also search for this author inPubMed Google Scholar * Jinming Luo View author publications You can also search for this author inPubMed Google Scholar CONTRIBUTIONS D.Y. and J.L. designed

research; D.Y. and L.X. performed the experiments; D.Y., L.X., X.L., K.F., S.W., M.W., W.L., C.L., and J.L. analyzed the data; and D.Y., L.X., and J.L. wrote the paper. All authors discussed

the results and commented on the manuscript. 1D.Y. and L.X. contributed equally to this work. CORRESPONDING AUTHOR Correspondence to Jinming Luo. ETHICS DECLARATIONS COMPETING INTERESTS The

authors declare no competing interests. PEER REVIEW PEER REVIEW INFORMATION _Nature Communications_ thanks the anonymous, reviewer(s) for their contribution to the peer review of this work.

A peer review file is available ADDITIONAL INFORMATION PUBLISHER’S NOTE Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional

affiliations. SUPPLEMENTARY INFORMATION SUPPLEMENTARY INFORMATION PEER REVIEW FILE REPORTING SUMMARY RIGHTS AND PERMISSIONS OPEN ACCESS This article is licensed under a Creative Commons

Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original

author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the

article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use

is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit

http://creativecommons.org/licenses/by/4.0/. Reprints and permissions ABOUT THIS ARTICLE CITE THIS ARTICLE Yu, D., Xu, L., Fu, K. _et al._ Electronic structure modulation of iron sites with

fluorine coordination enables ultra-effective H2O2 activation. _Nat Commun_ 15, 2241 (2024). https://doi.org/10.1038/s41467-024-46653-6 Download citation * Received: 23 September 2023 *

Accepted: 01 March 2024 * Published: 12 March 2024 * DOI: https://doi.org/10.1038/s41467-024-46653-6 SHARE THIS ARTICLE Anyone you share the following link with will be able to read this

content: Get shareable link Sorry, a shareable link is not currently available for this article. Copy to clipboard Provided by the Springer Nature SharedIt content-sharing initiative